Nhan đề: | Autogenous Deformation of Alkali-Activated Blast Furnace Slag Concrete Subjected to Variable Curing Temperatures |
Tác giả: | Orosz, Katalin Humad, Abeer Hedlund, Hans Cwirzen, Andrzej |
Từ khoá: | Humidity Shrinkage Temperature effects Slag Sodium Blast furnace slags Concrete research Stiffness Deformation Sodium silicates |
Năm xuất bản: | 2019 |
Nhà xuất bản: | Hindawi Publishing Corporation |
Tóm tắt: | Deformations of alkali-activated slag concrete (AASC) with high MgO and Al2O3 content, subjected to variable curing temperature were studied. Sodium silicate and sodium carbonate were used as alkali activators. The obtained results showed development of deformations consisting of both shrinkage and expansion. Shrinkage appeared not to be affected by the activator type, while the expansion developed after the cooling down phase in stabilized isothermal conditions and did not stop within the duration of the tests. X-ray diffraction analysis performed shortly after the cooling down phase indicated the formation of crystalline hydrotalcite, which was associated with the observed expansion. A mixture with a higher amount of sodium silicate showed less expansion, likely due to the accelerated hydration and geopolymerization leading to the increased stiffness of the binder matrix. |
Mô tả: | 8 tr. |
Định danh: | http://thuvienso.vanlanguni.edu.vn/handle/Vanlang_TV/16067 |
ISSN: | 1687-8086 1687-8094 (e) |
Bộ sưu tập: | Bài báo_lưu trữ |
Các tập tin trong tài liệu này:
Tập tin | Mô tả | Kích thước | Định dạng | |
---|---|---|---|---|
BBKH827_TCCN_Autogenous Deformation.pdf Giới hạn truy cập | Autogenous Deformation of Alkali-Activated Blast Furnace Slag Concrete Subjected to Variable Curing Temperatures | 1.58 MB | Adobe PDF | Xem/Tải về Yêu cầu tài liệu |
Khi sử dụng các tài liệu trong Thư viện số phải tuân thủ Luật bản quyền.